Pengaruh Penambahan POFA (Palm Oil Fuel Ash) dan Epoxy Untuk Mortar Dengan Perendaman Air Laut

Peri Hamdani; Cut Rahmawati; Tety Sriana

doi:10.30601/jtsu.v12i2.7772

Pengaruh Penambahan POFA (Palm Oil Fuel Ash) dan Epoxy Untuk Mortar Dengan Perendaman Air Laut

Peri Hamdani, Cut Rahmawati, Tety Sriana

Abstract

This study aims to analyze the effect of adding POFA (Palm Oil Fuel Ash) and epoxy on the mechanical properties of mortar immersed in seawater. POFA was utilized as a pozzolanic material to partially replace cement, while epoxy functioned as a polymer capable of enhancing bonding and densifying the mortar matrix. POFA and epoxy were added at variations of 0%, 10%, 20%, and 30%. The mortar was prepared with a cement-to-sand ratio of 1:2 and a water-cement ratio (w/c) of 0.65. Cube specimens measuring 5×5×5 cm were used for compressive strength testing, and beam specimens measuring 4×4×16 cm were used for flexural strength testing. All specimens were immersed in seawater prior to testing. The results showed that the addition of POFA and epoxy significantly influenced both compressive and flexural strength up to an optimum level. The highest compressive strength of 35.31 MPa was achieved in the mixture containing 10% POFA and 30% epoxy, while the maximum flexural strength of 0.91 MPa was obtained with 10% epoxy addition. However, excessive use of POFA and epoxy tended to reduce mechanical strength due to the decreased role of active cement and disruption of the hydration process. Therefore, the use of POFA and epoxy at optimum levels can produce more environmentally friendly mortar with improved durability and mechanical performance under seawater immersion.

Full Text:

PDF

References

Aditia, C. R., Elvira, & Rustamaji. (2024). "Analisis Kuat Tekan Resin Epoksi Campuran Agregat Halus Pasir Silika dan Pasir Biasa pada Mortar Polimer." Jurnal Teknik Sipil dan Lingkungan, 9(2). (Penelitian ini secara khusus membahas pengaruh epoxy pada kuat tekan mortar polimer).

Ahmad, A. B., & Hassan, S. M. (2018). Mechanical Properties of Mortar with Palm Oil Fuel Ash (POFA) as a Partial Cement Replacement. Journal of Civil Engineering, 15(2), 123-130.

Ahn, J., Lee, S., & Park, H. (2023). "Durability of polymer-modified concrete in chloride environment." Journal of Marine Structures, 8(2), 112-125.

Al-Jabri, A. S., Hago, A. W., & Al-Nuaimi, A. S. (2020). "Performance of concrete with palm oil fuel ash as a partial cement replacement." Construction and Building Materials, 239, 117865.

Arif, J., Husni, H. R., & Sebayang, S. (2015). Pengaruh Resin Epoksi Terhadap Mortar Polimer Ditinjau dari Kuat Tekan, Kuat Tarik Belah, Daya Serap Air dan Scanning Electron Microscope. Jurnal Rekayasa Sipil dan Desain, 3(3), 2303–2314.

Aulia, Z., Rahmawati, E., & Handayani, M. (2020). Pengaruh Penggunaan Abu Cangkang Sawit (POFA) sebagai Bahan Pengganti Semen terhadap Kuat Tekan dan Kuat Lentur Mortar. Jurnal Rekayasa Sipil, 6(1), 45-56.

Budianto, S., & Lestari, Y. (2019). "Studi Komparasi Kuat Tekan Mortar Normal dan Mortar dengan Penambahan Epoxy Resin." Prosiding Seminar Nasional Teknologi Sipil, 8(3), 210-218.

Ganesan, K., & Santhanam, M. (2015). "Enhancement of Mortar Properties using Epoxy Resin." Construction and Building Materials, 74, 25-33

Hassan, M. S., & Aziz, A. M. (2021). Palm Oil Fuel Ash-Based Eco-Friendly Concrete Composite: A Critical Review of the Long-Term Properties. Materials, 14(22), 7074.

Iswanti, A., 2015, Pengaruh Panambahan Pozzolan Terhadap Sifat Mekanis dan Absorpsi Beton Busa (Foamed Concrete), Universitas Syiah Kuala, Darussalam Banda Aceh.

Jayasena, J., Kularathna, R., & Wijesundara, L. (2021). "A review on the properties of palm oil fuel ash as a supplementary cementitious material." Journal of Building Engineering, 44, 103442.

Mehta, P. K., & Monteiro, P. J. M. (2014). Concrete: Microstructure, Properties, and Materials. McGraw-Hill Education. (Sumber ini memberikan wawasan mendalam tentang komposisi, mikrostruktur, dan karakteristik bahan-bahan konstruksi, termasuk semen dan mortar).

Mulyono, T., 2004, Teknologi Beton, Penerbit Andi, Yogyakarta.

Neville, A. M. (2011). Properties of Concrete. Prentice Hall. (Buku ini merupakan referensi klasik yang membahas secara mendalam tentang sifat-sifat beton dan material penyusunnya, termasuk mortar).

Nor, F. R., & Hamzah, I., Tan, T. S., & Lee, M. H. (2022). Optimal design of cement replacement using palm oil fuel ash with minimum embodied carbon and maximum mechanical properties.

Pai, B.H.V., Nandy, M., Krishnamoorthy, A., & Sarkar, P.K. (2014). Particle Packing Approach for Designing the Mortar Phase of Self Compacting Concrete. Makalah dipresentasikan pada International Conference on Sustainable Civil Infrastructure (ICSCI 2014).

Riyadi, F., & Widyawati, P. (2018). Pengaruh Variasi Persentase Epoxy terhadap Peningkatan Kuat Tekan dan Kuat Lentur Mortar. Jurnal Sains dan Teknologi, 5(1), 32-41.

S. F. Widayanti, E. F. Agustin, & A. N. Farida. (2022). Pengaruh Penambahan Serat Serabut Kelapa Terhadap Kuat Tarik Lentur Mortar Resin Epoksi.

Santos, P., Maceiras, A., Valvez, S., & Reis, P. N. B. (2021). Mechanical characterization of different epoxy resins enhanced with carbon nanofibers. Frattura ed Integrità Strutturale, 15(55), 198–212.

Taufik, R. (2021). Studi Penggunaan Abu Terbang (Fly Ash) dan Abu Cangkang Sawit (POFA) sebagai Bahan Pengisi Beton Ringan. Tesis, Universitas Gadjah Mada.

Troxell, G. E., Davis H. E., dan J. W. Kelly, 1968, Composition and Properties of Concrete, Mac Graw Hill Book Company, London.

Unaidi, M. Z., & Zulkifli, M. Z. (2021). Palm Oil Fuel Ash-Based Eco-Friendly Concrete Composite: A Critical Review of the Long-Term Properties. Materials, 14(22), 7074.

DOI: https://doi.org/10.30601/jtsu.v12i2.7772

Refbacks

There are currently no refbacks.

This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.

Jurnal Teknik Sipil Unaya

This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.